Activated Carbon Production and Chinoline Yellow Adsorption as a Result of Impregsion of Acasia Tree Sheath Growing ın Van and Area With Sodium Hydroxide


Creative Commons License

Genel İ., Genel Y.

10. Uluslararası Bilimsel Araştırmalar Kongresi, Ankara, Turkey, 11 - 12 April 2021, pp.51-60

  • Publication Type: Conference Paper / Full Text
  • City: Ankara
  • Country: Turkey
  • Page Numbers: pp.51-60
  • Van Yüzüncü Yıl University Affiliated: Yes

Abstract

In this study, the temperature, concentration and pH adsorption of quinoline yellow, which is used in food production but remained as waste in nature, by producing an activated carbon with high surface area and good pore volumes by using acacia wood chips in activated carbon production was investigated. In the study carried out, activated carbon with a surface area of 1389.0122 m2/g was produced as a result of imregnation of acacia wood shavings by mixing with NaOH at a ratio of 1: 1 and pyrolysis in nitrogen gas at 800 ° C in the production of activated carbon, Determining the maximum adsorption of quinoline yellow by activated carbon (q max), Langmuir The compatibility was observed according to the adsorption isotherm models of Freundlich, temkin and DR. The adsorption equilibrium data were best determined to be compatible with the Langmuir adsorption isotherm with R2 = 0.993 at 227.0390 mg / g and the kinetic model of the pseudo-second order kinetic model. Concentration measurements were made by UV spectrometer in the study. It has been observed that quinoline yellow gives different values in the spectrophotometer and the measurements are different, since it decomposes in acidic environment and changes color in basic environment. Since the pH of the dye is measured at 200ppm: 6.02, adsorption measurements were made at this pH. For this reason, it has been observed that the spectrophotometric measurements of the dyestuffs to be measured at different pH levels are important, and the potential of use of the produced activated carbon in dye removal is high

et Bu çalışmada Akasya ağaç talaşlarının aktif karbon üretiminde kullanılarak yüzey alanı yüksek, gözenek hacimleri iyi bir aktif karbon üretilerek gıda üretimde de kullanılan fakat doğada atık olarak kalan kinolin sarısının sıcaklık, konsantrasyon ve pH adsorpsiyonunu incelenmiştir. Yapılan çalışmada aktif karbon üretiminde akasya ağacı talaşının NaOH ile 1:1 oranında karıştırılarak imregnasyonu ve 800 ℃ de Azot gazı ortamında pirolizi sonucu yüzey alanı 1389.0122 m2/g olan aktif karbon üretilmiş, Aktif karbon tarafından maksimum kinolin sarısı adsorpsiyonu belirlenerek (q max), Langmuir, Freundlich, temkin ve D-R adsorpsiyon izoterm modellerine göre uyumu gözlendi. Adsorpsiyon denge verileri en iyi şekilde 227,0390 mg /g'de R2=0.993 değerine sahip Langmuir adsorpsiyon izotermiyle ve kinetik modelinin yalancı ikinci derecenden kinetik modele uyumlu olduğu belirlendi. Çalışmada konsatrasyon ölçümleri UV spektrometre ile yapılmıştır. Kinolin sarısının asidik ortamda parçalandığından ve bazik ortamda renk değişimine uğradığından dolayı spektrofotometrede farklı değerler verdiği ve ölçümler farklı olduğu gözlenmiştir. Boyar maddenin 200ppm de ölçülen pH:6,02 olduğundan adsorpsiyon ölçümleri bu pH’da yapılmıştır. Bu nedenle ölçümü yapılacak olan boyar maddelerin farklı pH’lardaki spektrofotometrik ölçümlerinin önemli olduğu, üretilen aktif karbonun boyarmadde gideriminde kullanım potansiyelinin yüksek olduğu gözlenmiştir