Characterization of the ITO/p-Si/Al contacts produced by thermal evaporation


Ozkartal A.

VACUUM, cilt.168, 2019 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 168
  • Basım Tarihi: 2019
  • Doi Numarası: 10.1016/j.vacuum.2019.108799
  • Dergi Adı: VACUUM
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Van Yüzüncü Yıl Üniversitesi Adresli: Evet

Özet

Indium-tin-oxide (ITO)/p-Si heterojunctions were produced by thermal evaporation using a vacuum coating unit. Cleaning process for the p-Si (1 0 0) crystal was carried out according to the conventional procedure. Prior to ITO evaporation, ohmic contact was made on the back side of the p-Si using Al (99.999%) metal. Optical transmission measurements of the ITO film was performed using a UV-Vis spectrophotometer. The fact that the ITO film shows a sharp absorbtion in a certain photon energy range points out it has a semiconductor property. So, optical band-gap of the ITO film was determined as 3.85 eV. The structural properties of the films were examined by x-ray diffraction spectroscopy (XRD). Current-voltage (I-V) measurements of . the ITO/p-Si heterojuntions were performed under illumination and in dark to reveal photovoltaic and electrical properties of them, respectively. It is discovered from the I-V measurements that the ITO/p-Si heterojuctions have shown rectifier properties and exhibited low photovoltaic characteristic.