RAFT-Mediated Synthesis and Temperature-Induced Responsive Properties of Poly(2-(2-Methoxyethoxy)ethyl Methacrylate) Brushes

Zengin A., Yildirim E., Caykara T.

JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY, cilt.51, sa.4, ss.954-962, 2013 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 51 Sayı: 4
  • Basım Tarihi: 2013
  • Doi Numarası: 10.1002/pola.26460
  • Dergi Adı: JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.954-962
  • Anahtar Kelimeler: atomic force microscopy, living polymerization, RAFT mediated polymerization, self assembly, temperature-responsive polymer brushes, THERMORESPONSIVE POLYMER BRUSHES, SILICON-WAFER SURFACE, GLYCOL) METHYL-ETHER, ISOPROPYLACRYLAMIDE BRUSHES, RADICAL POLYMERIZATION, N-ISOPROPYLACRYLAMIDE, MOLECULAR-WEIGHT, POLY(N-ISOPROPYLACRYLAMIDE), MEMBRANES, ADHESION
  • Van Yüzüncü Yıl Üniversitesi Adresli: Hayır

Özet

Well-defined, high-density poly(2-(2-methoxyethoxy) ethyl methacrylate) [poly(MEO(2M)A)] brushes were fabricated through a reliable strategy by the combination of self-assembly of a monolayer of 3-aminopropyltrimethoxy silane on silicon surface to immobilize 4-cyano-4-(dodecylsulfanylthiocarbonyl) sulfanyl pentanoic acid chain transfer agent and reversible addition-fragmentation chain transfer-mediated polymerization of MEO(2)MA. The whole fabrication process of the poly (MEO(2)MA) brushes was followed by water contact angle, grazing angle-Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, and atomic force microscopy. Characterization of the poly(MEO(2)MA) brushes, such as molecular weight and thickness determination, were measured by gel permeation chromatography and ellipsometry, and the grafting density was estimated. The temperature-responsive property of the poly(MEO(2)MA) brushes was further investigated and the result verified the brush-to-mushroom phase transition of the poly(MEO(2)MA) chains from low to high temperature. (C) 2012 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013, 51, 954-962